Research Project
Full description The present research examined the corrosion and crevice corrosion behaviour of porous specimens of Ti35Zr28Nb and CP Ti in Hanks' solution at 37 degrees C and in 3.5 wt% NaCl at 95 degrees C. The following conclusions can be drawn. There was no crevice corrosion for porous specimens of Ti35Zr28Nb and CP Ti in Hanks' solution at 37C and in 3.5 wt% NaCl at 95C. Both alloys had low corrosion rates in both solutions, and both alloys were passive in both solutions.